Duplex 2205 is a two-phase, ferritic, austenitic 22% chromium, 3% molybdenum, 5 to 6% nickel alloyed stainless steel. It is the most widely used duplex stainless steel grade and is characterized by high yield strength, double that of the standard austenitic stainless steel grades. It also demonstrates good fatigue strength, as well as outstanding resistance to stress corrosion cracking, crevice, pitting, erosion, and general corrosion in severe environments.
| Name | 304 Square Stainless Steel Tubing Seamless, stainless steel square tube |
| Items | ROUND SS SMLS PIPE |
| Standard | ASTM ,GB,DIN AISI |
| Material Grade | 201: Ni 0.7%--1% |
| 304: Ni 8%, Cr 18% |
| 316L:Ni10%,Cr16% |
| Outer Diameter | Round pipe9.5mm--813mm |
| Thickness | 0.8mm - 34mm |
| Length | 5.8m,6m, or as customers' request |
| Tolerance | a) Outer Diameter: +/- 0.2mm |
| b) Thickness: +/- 0.02mm |
| c) Length: +/- 5mm |
| Surface | annealing,pickling |
| | sandblasting |
| Application | industry,exhausting,water |
| Test | Squash test, extended test, water pressure test,heat treatment, NDT |
| Chemical Composition of Material | Material | 201 | 316L | 304 |
| C | ≤0.15 | ≤0.035 | ≤0.08 |
| Si | ≤1.00 | ≤1.00 | ≤1.00 |
| Mn | 5.5-7.5 | 2 | ≤2.00 |
| P | ≤0.06 | ≤0.045 | ≤0.045 |
| S | ≤0.03 | ≤0.03 | ≤0.03 |
| Cr | 16-18 | 16-18 | 18-20 |
| Ni | 3.5-5.5 | 10-14 | 8-11 |
| Mechanical Property | Material Item | 201 | 202 | |
| Tensile Strength | ≥535 | ≥520 | |
| Yield Strength | ≥245 | ≥205 | |
| Extension | ≥30% | ≥30% | |
| Hardness (HV) | <253 | <253 | |
Welding Characteristics
A. Possesses good weldability
B. Should not generally be welded without filler metal as this may result in excessive ferrite
Heat-Treatment
A. Annealing temperature range is 1868 to 2012°F (1020 to 1100°C)
B. Cannot be hardened by heat treatment – but Duplex 2205 does work-harden
C.Special consideration is needed to compensate for a higher coefficient of thermal expansion to avoid warping and distortion
Process -hot forming
Most Duplex 2205 producers recommend a maximum hot forming temperature between 2010 and 2100°F (1100 to 1150°C). If the shape of the work piece is not compact, the edges may be significantly cooler than the bulk, and there is risk of cracking in the cooler regions.
Process -Cold Forming
Duplex 2205 has shown good formability in a variety of fabrications. The high strength of Duplex 2205 can pose problems. Even when the equipment has sufficient power, allowance must be made for higher spring-back caused by the grade’s high strength.
Machinability
Duplex 2205 is somewhat more difficult to machine than the 300 series austenitic stainless steels. Higher cutting forces are required and more rapid tool wear is typical. Some guidelines for machining are: A) Use powerful, rigid machines with extremely strong rigid mounting of tools and work piece, B) Minimize vibration by keeping the tool extension as short as possible, C) Use a nose radius on the tool, no longer than necessary, for carbides that have a sharp edge while still providing adequate strength, D) Design machining sequences to always provide for a depth of cut below the work hardened layer resulting from the previous passes.